AS4
Vendor: Hexcel
·
Category: Glass Fiber
Mechanical
- Tensile strength
- 6000.00 MPa
- Tensile modulus
- 600.00 GPa
- Compressive strength
- 500.00 MPa
Toray T300 (UD Prepreg)
Vendor: Toray Industries
·
Category: Carbon Fiber
Mechanical
- Tensile strength
- 3530.00 MPa
- Tensile modulus
- 230.00 GPa
- Compressive strength
- 1500.00 MPa
- Flexural strength
- 1900.00 MPa
- Flexural modulus
- 200.00 GPa
- Shear strength
- 95.00 MPa
- Shear modulus
- 5.50 GPa
- Elongation at break
- 1.50 %
- ILSS
- 72.00 MPa
Physical
- Density
- 1.760 g/cm³
- Fiber areal weight
- 200 g/m²
- Fiber volume fraction
- 60.0 %
- Moisture absorption
- 0.10 %
Thermal
- Glass transition (Tg)
- 120 °C
- Decomposition (Td)
- 400 °C
- CTE
- 0.20 µm/m·°C
- Thermal conductivity
- 6.000 W/m·K
Electrical
- Electrical resistivity
- 0.00 Ω·cm
Processing
- Cure temp
- 120 °C
- Cure time
- 2h @ 120°C
- Viscosity
- Medium (epoxy resin system)