AF
Taparan® 529S 1110 dtex
Yantai Tayho ? High Tenacity
Manufacturer page / TDSDescription
Para-aramid filament yarn. Published tenacity ≥19.5 cN/dtex; elongation and modulus are nominal values with grade-specific tolerances.
Comparative overview
Aramid fiber — High-tenacity para-aramid
Strengths: Excellent specific tensile strength, toughness and energy absorption; fibers spread and dissipate impact energy while remaining dielectric and flame resistant.
When to use: Select for soft/hard armor, helmets, fragment protection, ropes, impact skins and hybrid laminates where toughness matters more than compression stiffness.
Key tradeoffs: Low compressive strength, moisture uptake, UV sensitivity and difficult machining/bonding; carbon is better for pure stiffness.
Qualitative ratings (1–10 scale)
| Relative cost | 8/10 — High — ballistic-grade para-aramid requires controlled spinning, yarn and finish quality. |
|---|---|
| EM transparency | 9/10 — Excellent — dielectric organic fiber suitable for RF-transparent structures when the matrix and moisture state are controlled. |
| Temperature / fire resistance | 6/10 — Good — flame resistant and non-melting, but organic decomposition limits sustained hot-section use. |
| Impact / penetration resistance | 10/10 — Top-tier — proven high-velocity penetration resistance and energy dissipation in soft and hard armor. Stored TDS elongation: 3.5%. |
| Electrical / thermal conductivity | 1/10 — Very low — electrically insulating with very low thermal transport. |
| Specific tensile strength | 7/10 — 7/10 | 1950.0 kN·m/kg | Product TDS |
| Atmospheric durability | 5/10 — Moderate — good chemical durability and no corrosion, but para-aramids require UV protection; humidity and the fiber–matrix interface can affect retained performance. |
| Sustainability (CO₂e) | 6/10 — 9.50 kg CO₂e/kg fiber — Medium emissions — data quality: Medium |
Technical properties
| Tensile strength | 2808.0 MPa |
|---|---|
| Tensile modulus | 90.0 GPa |
| Density | 1.44 g/cm³ |
Applications and processing
General industrial reinforcementGeneral industrial reinforcement